水雾预冷锌镀层22MnB5钢

Shi-da, Chen; Dong, Yikang; Yu-yang, Zhang; Zhen-dong, Cheng; Chen, Shoudong; Zhang, Sijia; Zhang, Guangji; Chen, Jingqi; Lu, Rihuan; Liu, Xianghua; Huang, Huagui

水雾预冷锌镀层22MnB5钢

抑制液态金属致脆

通过水雾预冷将锌镀层22MnB5热冲压钢的损伤模式从基体穿透开裂转变为涂层局限开裂，在保持高强度的同时防止脆断，实现高强度与延展性的最佳平衡。

Shi-da, Chen · Dong, Yikang · Yu-yang, Zhang · Zhen-dong, Cheng · 陈守东 · Zhang, Sijia · Zhang, Guangji · Chen, Jingqi · 卢日环 · Liu, Xianghua · Huang, Huagui

Materials Science & Engineering A: Structural Materials: Properties, Microstructure and Processing 2026

参数信息

temperature tensile strength: 10.0 MPa
tensile strength reduced: 10.2 MPa

技术优势

在750–720 °C喷淋终止温度下，主要损伤模式转变为涂层局限开裂

在680 °C喷淋终止温度下，未检测到基体穿透裂纹